Bismuth vanadate (BiVO4) is a promising photoanode material for the photoelectrochemical (PEC) water splitting. However its poor charge transfer transport and slow surface catalytic activity limit the expected theoretical efficiency. Herein we have investigated the effect of the type of electrolyte on the photoactivity of BiVO4 MoO3 photoanode. BiVO4 was deposited on indium tin oxide (ITO) using spin coating under the optimized experimental conditions and a thin layer of MoO3 was then deposited on BiVO4 by physical vapor deposition (PVD). Then the photoactivity of the BiVO4 MoO3 photoanode was examined in various electrolytes including KOH sodium nitrate (NaNO3) sodium sulfate (Na2SO4) and Na2SO4 containing tris(hydroxymethyl)aminomethane (Tris) solution. The results showed that the photocurrent densities were improved from few tens of μA cm-2 in Na2SO4 to 0.8 mA cm-2 in Na2SO4 solution containing Tris (Na2SO4-Tris).

کليدواژه ها

Photoelectrochemical water splitting BiVO4 MoO3 electrolyte

کد مقاله / لینک ثابت به این مقاله

برای لینک دهی به این مقاله، می توانید از لینک زیر استفاده نمایید. این لینک همیشه ثابت است :

نحوه استناد به مقاله

در صورتی که می خواهید در اثر پژوهشی خود به این مقاله ارجاع دهید، به سادگی می توانید از عبارت زیر در بخش منابع و مراجع استفاده نمایید:
عمران مرادلو , 1401 , فوتوآند BiVO4 MoO3 برای تولید هیدروژن از شکافت فوتوالکتروشیمیایی آب اثر الکترولیت , سومین کنفرانس ملی میکرو/نانوفناوری